Microarc Oxidation of the High-Silicon Aluminum AK12D Alloy

# 07, July 2015
DOI: 10.7463/0715.0779403
Article file: SE-BMSTU...o128.pdf (1043.35Kb)
authors: S.K. Kiseleva, L.I Zainullina, M.M. Abramova, N.Yu. Dudareva, I.V. Alexandrov

The aim of work is to study how the high-silicon aluminum AK12D alloy microstructure and MAO-process modes influence on characteristics (microhardness, porosity and thickness of the oxide layer) of formed surface layer.
Experimental methods of study:
  1) MAO processing of AK12D alloy disc-shaped samples. MAO modes features are concentration of electrolyte components – soluble water glass Na2SiO3 and potassium hydroxide (KOH). The content of two components both the soluble water glass and the potassium hydroxide was changed at once, with their concentration ratio remaining constant;
  2) metallographic analysis of AK12D alloy structure using an optical microscope «Olympus GX51»;
  3) image analysis of the system "alloy AK12D  MAO - layer" using a scanning electron microscope «JEOL JSM 6490LV»;
  4) hardness evaluation of the MAO-layers using a micro-hardness tester «Struers Duramin».
The porosity, microhardness and thickness of MAO-layer formed on samples with different initial structures are analyzed in detail. Attention is paid to the influence of MAO process modes on the quality layer.
It has been proved that the MAO processing allows reaching quality coverage with high microhardness values of 1200-1300HV and thickness up to 114 μm on high-silicon aluminum alloy.
It has been found that the initial microstructure of alloy greatly affects the thickness of the MAO - layer. The paper explains the observed effect using the physical principles of MAO process and the nature of silicon particles distribution in the billet volume.
It has been shown that increasing concentration of sodium silicate and potassium hydroxide in the electrolyte results in thicker coating and high microhardness. It has been revealed that high microhardness is observed in the thicker MAO-layers.
Conclusions:
  1) The microstructure of aluminum AK12D alloy and concentration of electrolyte components - liquid glass Na2SiO3 and potassium hydroxide affect the quality of coating resulted from MAO-processing.
  2) Increasing concentration of the electrolyte leads to the thicker MAO-layer of higher microhardness and lower porosity.
  3) Deformation-heat treatment of AK12D alloy samples using a scheme "forging + quenching + aging" before the MAO leads to deteriorated quality of formed layer.

References
  1. Zharinov P.M. Effektivnye mikrorazryady i novye sposoby naneseniya pokrytii na izdeliya iz alyuminievykh splavov. Avtoreferat kand. diss . [ Effective microdischarges and new methods for coating products made of aluminum alloys . Abstract of cand. diss.]. Moscow, 2009. 24 p. (in Russian, unpublished).
  2. Gabralla Mokhammed El'khag Mokhammed. Vliyanie elektricheskogo rezhima na svoistva mikrodugovykh pokrytii, formiruemykh na splave D16. Avtoreferat kand. diss . [ Influence of electrical conditions on the properties of microarc coatings formed on the alloy D16 . Abstract of cand. diss.]. Moscow, 2007. 24 p. (in Russian, unpublished).
  3. Tikhonenko V.V., Shkil'ko A.M. Method of microarc oxidation. Vostochno-Evropeiskii zhurnal peredovykh tekhnologii = Eastern-European Journal of Enterprise Technologies , 2012, vol. 2, no. 13 (56), pp. 13-18. (in Ukrainian).
  4. Dudareva N.Yu. Influence of modes microarc oxidation on properties of the formed surface. Vestnik UGATU , 2013, vol. 17, no. 3, pp. 217-222. (in Russian).
  5. Kuchmin I.B., Nechaev G.G. The current density as the determining parameter for the micro-arc oxidation process. Vestnik SSTU , 2013, vol. 1, no. 1 (69), pp. 62-66. (in Russian).
  6. Suminov I.V. Mikrodugovoe oksidirovanie: teoriya, tekhnologiya, oborudovanie [Microarc oxidation: theory, technology, equipment]. Moscow, Ekomet Publ., 2005. 368 p. (in Russian).
  7. Chigrinova N.M., Chigrinov V.E. Formation features of functional coatings in problem domains of metal structures for trade and advertising equipment. Proceedings of State Engineering University of Armenia. Ser. Mechanics, Machine Science, Machine-Building, 2012, iss. 15, no. 1, pp. 46-53. (in Russian).
  8. Krishtal M.M., Ivashin P.V., Polunin A.V., Pavlov D.A. Durability of parts from aluminium-silicon alloys improvement using micro arc oxidation for fuctioning in extremal friction conditions. Izvestiya Samarskogo nauchnogo tsentra Rossiiskoi akademii nauk , 2011, vol. 13, no. 4-3, pp. 765-768. (in Russian).
  9. Wenbin Xue, Xiuling Shia, Ming Huaa, Yongliang Lib. Preparation of anti-corrosion films by microarc oxidation on an Al-Si alloy. Applied Surface Science , 2007, vol. 253, no. 14, pp. 6118-6124. DOI: 10.1016/j.apsusc.2007.01.018
  10. Wenbin Xue, Chao Wangb, Hua Tiana, Yongchun Laia. Corrosion behaviors and galvanic studies of microarc oxidation films on Al-Zn-Mg-Cu alloy. Surface & Coatings Technology , 2007, vol. 201, iss. 21, pp. 8695-8701. DOI: 10.1016/j.surfcoat.2006.10.029
  11. Lei Wen, Yaming Wang, Ying Jin, Bing Liu, Yu Zhou, Dongbai Sun. Microarc oxidation of 2024 Al alloy using spraying polar and its influence on microstructure and corrosion behavior. Surface & Coatings Technology , 2013, vol. 228, pp. 92-99. DOI: 10.1016/j.surfcoat.2013.04.013
  12. Fedorov V.A., Velikosel'skaya N.D. Effect of the regimes of microarc treatment on the dimensions of friction pairs made of aluminum alloys. Khimicheskoe i neftyanoe mashinostroeni e, 1991, no. 5, pp. 24-26. (English version of journal: Chemical and Petroleum Engineering , 1991, vol. 27, iss. 5, pp. 280-283. DOI: 10.1007/BF01148552 ).
  13. Shundalov V.A., Ivanov V.Yu., Latysh V.V., Mikhailov I.N., Pavlinich S.P., Sharafutdinov A.V. Sposob polucheniya ul'tramelkozernistykh zagotovok iz metallov i splavov [Method of obtaining ultrafine-grained billets made of metals and alloys]. Patent RF, no. 2393936, 2010. (in Russian).
  14. Tokarev A.V. Electrophysical characteristics of aluminum cover obtained by microarc oxidation method. Vestnik KRSU , 2012, vol. 12, no. 10, pp. 106-110. (in Russian).
  15. Saltykov S.A. Stereometricheskaya metallografiya [Stereometric metallography]. Moscow, Metallurgiya Publ., 1976. 271 p. (in Russian).
  16. Epel'fel'd A.V. Use of micro-arc oxidation technology for forming protective coatings . High Energy Flows Material Processing: website. Available at: http://tompve.ru/science/techn_mash.htm, accessed 18.02.2015. (in Russian).
  17. Alekhin V.P., Fedorov V.A., Bulychev S.I, Tyurpenko O.A. Features of the microstructure of the hardened surface layers obtained by microarc oxidation. Fizika i khimiya obrabotki materialov = Physics and Chemistry of Materials Treatment , 1991, no. 5, pp. 121-126. (in Russian).
  18. Krishtal M.M. Thermal conductivity of oxide coatings obtained by micro-arc oxidation, on silumin AK9. Vektor nauki TGU , 2012, no. 4 (22), pp. 169-172. (in Russian).
  19. Lelevkin V.M., Tokarev A.V., Chertkova A.A. Carbon-oxide composite coating on aluminum. Vestnik KRSU , 2012, vol. 12, no. 5, pp. 166-169. (in Russian).
  20. Krishtal M.M., Ryumkin M.O. Influence of the starting structure of Al-Si alloys on the properties of oxide layers obЬнtained by the microarc oxidation, and retardation of the oxide growth by the silicon particles. Materialovedenie , 2008, no. 12, pp. 50-61. (in Russian).

 

Поделиться:
 
SEARCH
 
elibrary crossref ulrichsweb neicon rusycon
Photos
 
Events
 
News



Authors
Press-releases
Library
Conferences
About Project
Rambler's Top100
Phone: +7 (915) 336-07-65 (строго: среда; пятница c 11-00 до 17-00)
  RSS
© 2003-2024 «Наука и образование»
Перепечатка материалов журнала без согласования с редакцией запрещена
 Phone: +7 (915) 336-07-65 (строго: среда; пятница c 11-00 до 17-00)